Interior Tub of a Top-Loading

 

Washing Machine The interior tub of a washing machine is the container that holds the clothes during the washing and rinsing cycles, but it also contains the perforations that permit removal of the water by draining and spinning. The component will see mechanical loadings from the weight of the clothes and water, and also the dynamic action of spinning water-laden fabrics. There will be exposure to a wide range of water quality, as well as the full spectrum of soaps, detergents, bleaches, and other laundry additives. The surfaces should also be resistant to the impact and abrasion of buttons, zippers, and snaps. This part has traditionally been manufactured by the sequential deep drawing, perforating, and trimming of metal sheet, followed by some form of surface-coating treatment. For a long time, the standard material was “enameling iron”—a steel sheet with less than 0.03% carbon that was then coated with a fired porcelain enamel. Due to the difficulties of producing ultra-low-carbon material in today’s steelmaking operations, enameling iron became increasingly scarce, and manufacturers were forced to substitute the lowest-carbon, most readily available material, namely 1008 steel. This substitution further required modification of the enameling process to prevent defects and blistering from CO evolution. Your employer is presently manufacturing these tubs from 1008 steel sheet with a subsequent coating of fired porcelain enamel.Your marketing staff, however, reports that consumers tend to view a stainless steel tub to be of higher quality. As a result, your supervisor has asked you to evaluate the merits of converting to this material.You must first familiarize yourself with the current product (the base material, the forming process, and the porcelain enameling), and then determine what might be involved in converting to stainless steel. Consider the following specific questions:

1. What are the obvious pros and cons of the present product and process? Where would you expect most problems to occur in the current manufacturing process? Which aspects of fabrication are likely to be the most costly?

2. What would be the pros and cons of converting to stainless steel? In what ways would the product be superior? Are there any assets or liabilities associated with product fabrication from stainless material?

3. Which stainless steel would you recommend? Begin by considering the basic types (ferritic, austenitic, and martensitic) and then refine your selection to a specific alloy if possible. Discuss the rationale for your selection.

4. Since deep drawing is a metal deformation process, we could use cold working (strain hardening) as a strengthening mechanism. Would you find this to be attractive, or would you prefer to use a recrystallization anneal after drawing and prior to use? Why? If you elect to use cold work, might you want to at least perform a stress-relief heat treatment prior to use? Could this be done and still preserve the deformation strengthening? In deep drawing, the deformation is not uniform (increasing as we move up the sidewalls of the container), and the bottom of the tub simply retains the properties of the starting sheet. In order to ensure a minimum amount of strength at all locations, it may be desirable to begin the drawing with a partially cold-rolled sheet. Do you find this suggestion to be desirable? Why or why not?

5. After drawing and perforating, the residual drawing lubricant is removed from the part. Would any additional surface treatment be required? What would be your recommendation?